Investigation of the Effects of some Parameters in the Production of Chromate from Chromite Ores in Iskenderun Region

The conversion of chromite ore from iskenderun region into chromate was investigated. Firstly, the chromite ore was analysed using conventional chemical methods. Then, the effect of some parameters such as roasting time, temperature and the amount of additives on the conversion efficiency to the chromate was examined. The optimum roasting conditions were determined as 300°C, 2 hours, 10 times the stoichiometrically required amounts of NaClO₃ and 6 times the stoichiometrically required amounts of KOH. Under these conditions, the maximum recovery of chromate was found to be 100%. The product obtained from the roasting process was leached with water to produce a clean chromate solution. The effect of temperature and solid/liquid (S/L) ratio was investigated in the water leaching experiments. The optimum experimental results obtained were 100% at a 1:5 solid to water ratio at 25°C and 20 min leaching period. The chromate solution was purified using conventional purification processes.     

某硅线石矿石选别中除铁研究

针对矿石中硅线石微细嵌布，铁矿物嵌布亦较细。且有近二分之一铁在非金属矿物晶格之中，除铁难的特点，通过试验研究对比采用一段磨矿磁选除铁后磁尾浮选富集硅线石．浮选精矿再磨后酸浸再除铁的工艺方法，获得了理想的除铁效果，使硅线石精矿质量达到较高品质。     

浅析铂钯精矿的提取技术

本文简述湿法工艺提取铂钯金属精矿的工艺技术及主要生产过程     

The effects of soaking of whole, dehulled and ground millet and soybean seeds on phytate degradation and Phy/Fe and Phy/Zn molar ratios

The degradation and leaching of phytates, phytase activity and iron and zinc concentrations have been studied after soaking of whole seeds, dehulled seeds and flours of millet and soybean, in order to investigate the efficiency of soaking on reducing Phy/Fe and Phy/Zn molar ratios. When using millet grains, dehulling and milling before soaking facilitated the leaching of phytates and phytases in the aqueous medium and hence phytate degradation. Dehulling of soybean seeds led to a marked increase in phytate content, whereas milling favoured reactions between phytases and phytates. The Phy/Fe and Phy/Zn molar ratios decreased only slightly during soaking. The highest decreases for millet were obtained after soaking of flour for 8 h (Phy/Fe: 10.8–7.7 and Phy/Zn: 20.3–15.1), and after soaking of whole seeds for 24 h for soybean (Phy/Fe: 10.4–9.4 and Phy/Zn: 23.8–19.1). Cooking of flours with water used for soaking did not increase phytate degradation.     

辉锑矿矿浆电解浸出机理的研究

研究了辉锑矿矿浆电解阳极室浸出反应机理．结果表明，辉锑矿的溶解符合核收缩模型的动力学规律，浸出速率受混合过程控制，表观活化能为25.10KJ/mol．浸出主反应是辉锑矿被阳极上析出的氯氧化，SCl2是氧化反应的中间产物．     

镇沅金精矿选择性固砷焙烧—氰化浸出新工艺研究

对云南镇沅金矿的难当金精矿进行了选择性固砷焙烧－氰化浸出的试验研究，取得了满意结果。砷固定率大于９２％，硫挥发率为７８％－８４％，金浸出率可达９１％－９３％。选择性固砷焙烧－氰化浸出新工艺可有效消除砷害，综合利用有价成分硫，特别适宜于含砷高硫，同时含碳等杂质的细粒浸染型难浸金矿石的处理，在我国有较大的发展前景。     

大豆蛋白分离工艺研究

阐述了大豆蛋白质的分离原理,分析了运用“碱提酸沉”分离法提取大豆蛋白质过程中,豆粕的粉碎方式、浸提温度、浸提时间、浸提液的pH值以及离心工艺对提取效果的影响,为大豆蛋白／聚丙烯腈纤维的工业化生产提供了依据。     

从氯化铅渣中回收铅铋的研究

本文以柿竹园有色金属矿粗铋火法精炼、气化除铅产出的铅渣为原料，在常压下采用氯化钠水溶液进行浸出处理，有效地分离了铅和铋，并将铅制成了化工产品黄丹及硫酸铅     

硫脲法从低品位含金硫化矿及其焙砂酸浸渣中回收金

本工作采用硫脲法从钴铜硫化矿及其经硫酸化焙烧,酸浸钴铜后的渣中对低品位金进行了浸取研究.直接浸取硫化矿,金的溶出率低,操作参数如电位、pH值等不稳定,试剂耗量大;而从酸浸渣中浸取金的溶出率高,可达91.0%以上,数据重现性好,试剂消耗大大降低,操作稳定.优化了浸取条件,从而降低了硫脲消耗,耗量是1.78kg/t矿.最后,用还原铁粉和活性炭从硫脲浸取富液中回收金进行了探索,效果良好.试验结果表明,硫脲法具有潜在的工业性应用推广价值.     

从铜镉渣中回收镉的试验研究

本文介绍了从铜镉渣中回收镉的试验研究情况，采用酸浸-铜镉渣中和-锌粉除铜法处理铜镉渣，工艺简单合理，镉直收率高，有一定的推广价值。